CSS-1h Furol Viscosity @ 25 C, sec. Residue by Weight, % Cement Mixing Test, % Particle Charge Test 35 64.5 0.8 0.9 ASTM D 6935-04 Penetration @ 25 C, dmm. Solubility, % Ductility @ 25 C 60 99.9 100+ ASTM D 2042-01 ASTM D 113-99
CSS-1hm Furol Viscosity @ 25 C, sec. Residue by Weight, % Particle Charge Test 41 64.1 0.5 Penetration @ 25 C, dmm. Solubility, % Ductility @ 25 C Softening Point F 62 99.9 100+ 145 ASTM D 2042-01 ASTM D 113-99 ASTM D 36-95
CSS-1hp Furol Viscosity @ 25 C, sec. Residue by Weight, % Particle Charge Test 41 64.1 0.5 Penetration @ 25 C, dmm. Elastic Recovery, 10ºC, % Solubility, % Ductility @ 25 C Softening Point F 62 65 99.9 100+ 145 ASTM D 6084-04 ASTM D 2042-01 ASTM D 113-99 ASTM D 36-95
A S P H A L T R E P O R T PG 64-22 TEST Original Binder RESULT SPECIFICATION Flash Point, T48, C 250+ 230 Min. Specific Gravity, ASTM D70, 60 C 1.0311 -- Viscosity, ASTM D4402, 135 C, Pa.s 1.6 3.0 Max. Dynamic Shear, TP5, G*/sinδ, kpa, 10 rad/s, 64 C 1.14 1.00 Min. Phase Angle, degree 63.0 Report Penetration, ASTM D5, 25 C 62 55-75 RTFOT Residue Mass Loss, % 0.11 1.00 Max. Dynamic Shear, TP5, G*/sinδ, kpa, 10 rad/sec, 70 C 2.6 2.20 Min. PAV (100 C) Residue) Dynamic Shear, TP5, G*/sinδ, kpa, 10 rad/sec, 25 C 3,000 5,000 Max. Creep Stiffness, TP1, m -12 C 0.328.300 Min. Creep Stiffness, TP1, S, Mpa -12 C 170 300 Max.
SAMI Furol Viscosity @ 50 C, sec. Residue by Distillation, % Oil by Volume, % Particle Charge Demulsibility, 33 ml, 0.8%, Sodium Dioctyl Sulfosuccinate, % 240 70.5 0.25 0.2 75.0 ASTM D 6937-04 Penetration, 25 C, dmm. Force Ductility, 4 C, 40cm, lbs./sq.in. Elastic Recovery, 4ºC, % Softening Point, ºC 95 25+ 73 68 AASHTO T 300 ASTM D 6084-04 ASTM D 36-95
Job Number: 10010AOM Date: 3/23/2015 Company: Description: PASS QB EMULSION REPORT Test on Emulsion Concentrate Method Specification Viscosity, Saybolt Furol at 25 C [77 F] SFS ASTM D7496 20-100 Residue, %, min. ASTM D6997 65 Particle Charge Test ASTM D7402 Sieve Test, %, max. ASTM D6933 0.1 Oil distillate, %, max. ASTM D6997 0.5 Specific Gravity of residue of recovered latex, min. WE-EM 100-2 1.15 Test on Residue (1) Method Specification Penetration, 25 C [77 F], min. ASTM D5 70 Penetration, 4 C [39.2 F], report ASTM D5 - Elastic Recovery, 10 C [50 F], %, min. ASTM D6084 45 Test on Emulsion Diluted Method Specification Residue, % ASTM D6997 30-35 Sieve Test, %, max. ASTM D6933 0.05 Test on Latex Method Specification Specific Gravity, min. ASTM 1475 1.08 Tensile strength, die C dumbbell, psi, min. ASTM D412 500 Swelling in rejuvenating agent, %, max., 48 hours ASTM D471 40% exposure @ 104 F Modified Intact Film Test on Rejuvenating Agent Method Specification Flash point, COC, F ASTM D92 > 380 Hot Mix Recycling Agent Classification ASTM D4552 See Section II
Job Number: 10010AOM Date: 3/23/2015 Company: Description: PASS CR EMULSION REPORT Test on Emulsion Method Specification Viscosity, Saybolt Furol at 50 C [122 F] ASTM D7496 75-450 Residue, %, min. ASTM D6997 (1) 65 Particle Charge Test ASTM D7402 Sieve Test, %, max. ASTM D6933 0.1 Oil Distillate, %, max. ASTM D6997 1.0 Demulsibility, DSS, 35 ml, %, min. ASTM D6936 50 Specific Gravity of residue of recovered latex, min. WE-EM 100-2 (5) 1.15 Test on Residue (1) Method Specification Penetration, 25 C [77 F], min. ASTM D5 80 Penetration, 4 C [39.2 F], report ASTM D5 - Elastic Recovery, 10 C [50 F], %, min. ASTM D6084 (2) 45 Test on Latex Method Specification Specific Gravity, min. ASTM 1475 1.08 Tensile strength, die C dumbbell, psi, min. ASTM D412 (3) 500 Swelling in rejuvenating agent, %, max., 48 hours ASTM D471 (4) 40% exposure @ 104 F Modified Intact Film Test on Rejuvenating Agent Method Specification Flash point, COC, F ASTM D92 > 380 Hot Mix Recycling Agent Classification ASTM D4552 See Section II