KLINGER soft-chem KLINGER soft-chem brings the sealing technology on a new level and it is the best choice for operating conditions up to 260 C. Multi-directional expanded PTFE Excellent corrosion resistance together with superior sealability create a high-grade gasket material for a wide field of applications in your plant. Key features: Benefits: Multi-directional expanded PTFE Suitable for a wide range of applications Easy to cut Excellent sealing at low stress Seals irregular flanges No ageing of the material Certificates and approvals: Properties: referring to KLINGER top-chem product range Conforms to the regulation (EU) No. 935/2004 (incl. 0/20) FDA conformity (components of KLINGER softchem comply with the FDA requirements) SUPERIOR EXCELLENT VERY GOOD GOOD MODERATE MECHANICAL THERMAL SEALABILITY Industries: INDUSTRY OIL & GAS ENERGY INFRASTRUCTURE PULP & PAPER TRANSPORT FOOD & BEVERAGES PHARMA
Typical technical data for thickness 2.0 mm: Compressibility ASTM F 36 M % -60 Recovery ASTM F 36 M % 3-7 Stress relaxation DIN 5293 30 MPa, 6 h/ C MPa 5 KLINGER cold/hot compression thickness decrease at 23 C % 35 25 MPa thickness decrease at C % 30 Tightness DIN 28090-2 mg/s x m 0.00 Density g/cm 3 0.9 Dimensions of the standard sheets: Sizes: 0 x 0 mm Thicknesses:.5 mm, 2.0 mm, 3.0 mm Tolerances: Thickness 0% Length mm, width mm Other thicknesses, sizes and tolerances on request. pt diagram for thickness 2.0 mm: 00 90 80 70 60 40 3 In area one, the gasket material is normally suitable subject to chemical compatibility. 2 3 In area two, the gasket material may be suitable but a technical evaluation is recommended. In area three, do not install the gasket without a technical evaluation. Always refer to the chemical resistance of the gasket to the media. 30 20 2 p i bar 0-200 -00 0 C 00 200 300 400 Certified acc. to DIN EN ISO 900:2008 Subject to technical alterations. Status: March 206 Rich. Klinger Dichtungstechnik GmbH & Co KG» Am Kanal 8-0» A-2352 Gumpoldskirchen, Austria Tel +43 (0) 2252/62599-37» Fax +43 (0) 2252/62599-296» e-mail: marketing@klinger.co.at
KLINGER top-chem 2000soft KLINGER top-chem 2000soft combines the best load bearing capacity with excellent compressibility. It consists of a unique matrix which creates a universal heavy duty gasket. Porous PTFE filled with silicon carbide. Superior chemical resistance in strongly acidic and alkaline applications. It shows exceptional performance in applications with high mechanical requirements at high temperatures. KLINGER top-chem 2000soft has a high conformability and is ideal for maintaining a tight seal even at low surface loads. Key features: Benefits: Resistant to creep and cold flow High compressibility Mechanically stable Consistent material composition Resists high surface pressure also at elevated temperatures Provides excellent adaptability to any sealing surface High retention of the bolt load Superior chemical resistance No ageing of the material Certificates and approvals: Properties: referring to KLINGER top-chem product range TA-Luft (Clean air): in progress FDA conformity: in progress Regulation (EU) No. 935/2004 (incl. 0/20): in progress SUPERIOR EXCELLENT VERY GOOD GOOD MODERATE MECHANICAL THERMAL SEALABILITY Industries: INDUSTRY OIL & GAS ENERGY INFRASTRUCTURE PULP & PAPER TRANSPORT FOOD & BEVERAGES PHARMA
Typical technical data for thickness 2.0 mm: Compressibility ASTM F 36 M % 5 Recovery ASTM F 36 M % 20 Stress relaxation DIN 5293 MPa, 6 h/260 C MPa 30 30 MPa, 6 h/ C MPa 25 KLINGER cold/hot compression thickness decrease at 23 C % 7 MPa thickness decrease at 260 C % 20 Tightness DIN 28090-2 mg/s x m 0.05 Thickness/weight increase H 2 SO 4, 00%: 8 h/23 C % / HNO 3, 00%: 8 h/23 C % /2 NaOH, 33%: 72 h/0 C % 2/3 H 2 O: 5 h/00 C % / Dimensions of the standard sheets: Sizes: 0 x 0 mm Thicknesses:.5 mm, 2.0 mm, 3.0 mm Tolerances: Thickness acc. DIN 2809- Length mm, width mm Other thicknesses, sizes and tolerances on request. pt diagram for thickness 2.0 mm: 200 00 90 80 70 60 40 30 3 2 In area one, the gasket material is normally suitable subject to chemical compatibility. 2 3 In area two, the gasket material may be suitable but a technical evaluation is recommended. In area three, do not install the gasket without a technical evaluation. Always refer to the chemical resistance of the gasket to the media. 20 p i bar 200 00 0 C 00 200 2 Certified acc. to DIN EN ISO 900:2008 Subject to technical alterations. Status: March 206 Rich. Klinger Dichtungstechnik GmbH & Co KG» Am Kanal 8-0» A-2352 Gumpoldskirchen, Austria Tel +43 (0) 2252/62599-37» Fax +43 (0) 2252/62599-296» e-mail: marketing@klinger.co.at
KLINGER top-chem 2000 KLINGER top-chem 2000 is a universal heavy-duty gasket, which offers an exceptional performance in applications with high mechanical requirements at high temperatures. The only PTFE gasket with a Fire-safe-certificate. PTFE gasket filled with SiC (Silicon carbide). Excellent resistance in strongly acidic and alkaline applications as well as to steam and oxygen. Suitable for an extremely wide range of applications in the chemical and petrochemical industry, as well as in the ship building industry for the transport of chemicals. Key features: Benefits: Mechanically stable Resistant to creep and cold flow Consistent material composition Resists high surface pressure also at elevated temperatures High retention of the bolt load Superior chemical resistance No ageing of the material Certificates and approvals: Properties: referring to KLINGER top-chem product range BAM-tested DIN-DVGW DIN-DVGW W 270 KTW-Guideline German Lloyd TA-Luft (Clean air) Fire-Safe acc. DIN EN ISO 0497 FDA conformity (for details please see our website) Regulation (EU) No. 935/2004 (incl. 0/20) SUPERIOR EXCELLENT VERY GOOD GOOD MODERATE MECHANICAL THERMAL SEALABILITY Industries: INDUSTRY OIL & GAS ENERGY INFRASTRUCTURE PULP & PAPER TRANSPORT FOOD & BEVERAGES PHARMA
Typical technical data for thickness 2.0 mm: Compressibility ASTM F 36 M % 4 Recovery ASTM F 36 M % Stress relaxation DIN 5293 30 MPa, 6 h/ C MPa 28 MPa, 6 h/300 C MPa 35 KLINGER cold/hot compression thickness decrease at 23 C % 5 MPa thickness decrease at 2 C % Tightness DIN 28090-2 mg/s x m 0.08 Specific leakrate λ VDI 2440 mbar x l/s x m 4.46E-06 Thickness/weight increase H 2 SO 4, 00%: 8 h/23 C % / HNO 3, 00%: 8 h/23 C % /2 NaOH, 33%: 72 h/0 C % /3 Density g/cm 3 2.5 Average surface resistance ρo Ω 6.9x0E2 Average specific volume resistance ρd Ω cm 2.2x0E2 Average dielectric strength E d kv/mm 3.6 Average power factor Hz tan δ 0.66 Average dielectric coefficient Hz εr 0.6 Thermal conductivity λ W/mK 0.60 ASME-Code sealing factors for gasket thickness.0 mm tightness class 0.mg/s x m MPa y 2 m 2.8 for gasket thickness 2.0 mm tightness class 0.mg/s x m MPa y 5 m 3.2 for gasket thickness 3.0 mm tightness class 0.mg/s x m MPa y 8 m 3.8 Dimensions of the standard sheets: Sizes: 0 x 0 mm Thicknesses:.0 mm,.5 mm, 2.0 mm, 3.0 mm Tolerances: Thickness acc. DIN 2809- Length mm, width mm Other thicknesses, sizes and tolerances on request. pt diagram for thickness 2.0 mm: 200 00 90 80 70 60 40 3 2 In area one, the gasket material is normally suitable subject to chemical compatibility. 2 3 In area two, the gasket material may be suitable but a technical evaluation is recommended. In area three, do not install the gasket without a technical evaluation. Always refer to the chemical resistance of the gasket to the media. 30 20 p i bar 200 00 0 C 00 200 2 Certified acc. to DIN EN ISO 900:2008 Subject to technical alterations. Status: March 206 Rich. Klinger Dichtungstechnik GmbH & Co KG» Am Kanal 8-0» A-2352 Gumpoldskirchen, Austria Tel +43 (0) 2252/62599-37» Fax +43 (0) 2252/62599-296» e-mail: marketing@klinger.co.at
KLINGER top-chem 2003 KLINGER top-chem 2003 offers a high adaptability and tightness even at low surface loads. PTFE filled with hollow glass-microspheres. Excellent chemical resistance in strongly acidic and alkaline applications as well as very good properties at medium temperatures and loads. Key features: Benefits: High compressibility Consistent material composition Resistant to cold flow Excellent sealing at low stress Superior chemical resistance Conforms easily Provides superior adaptability to any sealing surface No ageing of the material Certificates and approvals: Properties: referring to KLINGER top-chem product range BAM tested DIN-DVGW DIN-DVGW W 270 KTW-Guideline German Lloyd TA-Luft (Clean air) FDA conformity (components of KLINGER topchem 2003 comply with the FDA requirements) Regulation (EU) No. 935/2004 (incl. 0/20) SUPERIOR EXCELLENT VERY GOOD GOOD MODERATE MECHANICAL THERMAL SEALABILITY Industries: INDUSTRY OIL & GAS ENERGY INFRASTRUCTURE PULP & PAPER TRANSPORT FOOD & BEVERAGES PHARMA
Typical technical data for thickness 2.0 mm: Compressibility ASTM F 36 M % 8 Recovery ASTM F 36 M % 35 Stress relaxation DIN 5293 30 MPa, 6 h/ C MPa 3 KLINGER cold/hot compression thickness decrease at 23 C % 9 25 MPa thickness decrease at 2 C % 36 Tightness DIN 28090-2 mg/s x m 0.0 Specific leakrate λ VDI 2440 mbar x l/s x m 3.29E-06 Thickness/weight increase H 2 SO 4, 00%: 8 h/23 C % / HNO 3, 00%: 8 h/23 C % 0/5 NaOH, 33%: 72 h/0 C % /5 Density g/cm 3.7 Average surface resistance ρo Ω 9x0E2 Average specific volume resistance ρd Ω cm 2.6x0E2 Average dielectric strength E d kv/mm 6.7 Average power factor Hz tan δ 0.085 Average dielectric coefficient Hz εr 2.8 Thermal conductivity λ W/mK 0.8 ASME-Code sealing factors for gasket thickness.0 mm tightness class 0.mg/s x m MPa y 8.0 m 2.0 for gasket thickness 2.0 mm tightness class 0.mg/s x m MPa y 8.0 m 2.7 for gasket thickness 3.0 mm tightness class 0.mg/s x m MPa y 0 m 3.6 Dimensions of the standard sheets: Sizes: 0 x 0 mm Thicknesses:.0 mm,.5 mm, 2.0 mm, 3.0 mm Tolerances: Thickness acc. DIN 2809- Length mm, width mm Other thicknesses, sizes and tolerances on request. pt diagram for thickness 2.0 mm: 200 00 90 80 70 60 3 2 In area one, the gasket material is normally suitable subject to chemical compatibility. 2 3 In area two, the gasket material may be suitable but a technical evaluation is recommended. In area three, do not install the gasket without a technical evaluation. Always refer to the chemical resistance of the gasket to the media. 40 30 20 p i bar 200 00 0 C 00 200 2 Certified acc. to DIN EN ISO 900:2008 Subject to technical alterations. Status: March 206 Rich. Klinger Dichtungstechnik GmbH & Co KG» Am Kanal 8-0» A-2352 Gumpoldskirchen, Austria Tel +43 (0) 2252/62599-37» Fax +43 (0) 2252/62599-296» e-mail: marketing@klinger.co.at
KLINGER top-chem 2005 KLINGER top-chem 2005 offers an outstanding performance and a high chemical resistance in strongly acidic applications. PTFE filled with inorganic fillers. Suitable for a wide range of applications in the chemical industry. Economical alternative at the usage of filled PTFE gaskets. Key features: Benefits: Mainly for use in acids Consistent material composition Resistant to cold flow Excellent chemical resistance Very good mechanical properties at medium temperatures No ageing of the material Certificates and approvals: Properties: referring to KLINGER top-chem product range BAM-tested DIN-DVGW WRAS approval KTW-Guideline German Lloyd TA-Luft (Clean air) FDA conformity (components of KLINGER topchem 2005 comply with the FDA requirements) Regulation (EU) No. 935/2004 (incl. 0/20) SUPERIOR EXCELLENT VERY GOOD GOOD MODERATE MECHANICAL THERMAL SEALABILITY Industries: INDUSTRY OIL & GAS ENERGY INFRASTRUCTURE PULP & PAPER TRANSPORT FOOD & BEVERAGES PHARMA
Typical technical data for thickness 2.0 mm: Compressibility ASTM F 36 M % 4 Recovery ASTM F 36 M % 40 Stress relaxation DIN 5293 30 MPa, 6 h/ C MPa 25 KLINGER cold/hot compression thickness decrease at 23 C % 5 MPa thickness decrease at 2 C % 33 Tightness DIN 28090-2 mg/s x m 0.02 Specific leakrate λ VDI 2440 mbar x l/s x m 8.75E-07 Thickness/weight increase H 2 SO 4, 00%: 8 h/23 C % / HNO 3, 00%: 8 h/23 C % /2 NaOH, 33%: 72 h/0 C % Density g/cm 3 2.2 Average surface resistance ρo Ω 3.x0E3 Average specific volume resistance ρd Ω cm 3.2x0E3 Average dielectric strength E d kv/mm 23.8 Average power factor Hz tan δ 0.07 Average dielectric coefficient Hz εr 3.2 Thermal conductivity λ W/mK 0.42 ASME-Code sealing factors for gasket thickness.0 mm tightness class 0.mg/s x m MPa y 0 m 2.2 for gasket thickness 2.0 mm tightness class 0.mg/s x m MPa y 2 m 2.8 for gasket thickness 3.0 mm tightness class 0.mg/s x m MPa y 2 m 3.8 Dimensions of the standard sheets: Sizes: 0 x 0 mm Thicknesses:.0 mm,.5 mm, 2.0 mm, 3.0 mm Tolerances: Thickness acc. DIN 2809- Length mm, width mm Other thicknesses, sizes and tolerances on request. pt diagram for thickness 2.0 mm: 200 00 90 80 70 60 40 3 2 In area one, the gasket material is normally suitable subject to chemical compatibility. 2 3 In area two, the gasket material may be suitable but a technical evaluation is recommended. In area three, do not install the gasket without a technical evaluation. Always refer to the chemical resistance of the gasket to the media. 30 20 p i bar 200 00 0 C 00 200 2 Certified acc. to DIN EN ISO 900:2008 Subject to technical alterations. Status: March 206 Rich. Klinger Dichtungstechnik GmbH & Co KG» Am Kanal 8-0» A-2352 Gumpoldskirchen, Austria Tel +43 (0) 2252/62599-37» Fax +43 (0) 2252/62599-296» e-mail: marketing@klinger.co.at
KLINGER top-chem 2006 KLINGER top-chem 2006 offers an excellent resistance in strongly alkaline applications and good mechanical properties at medium and low temperatures and loads. PTFE filled with Barium sulphate. Suitable for a wide range of applications in the chemical industry. This gasket material is free from pigments. Key features: Benefits: Mainly for use in alkaline media Consistent material composition Resistant to cold flow Excellent chemical resistance Very good mechanical properties at medium temperatures No ageing of the material Certificates and approvals: Properties: referring to KLINGER top-chem product range BAM-tested DIN-DVGW German Lloyd TA-Luft (Clean air) FDA conformity (components of KLINGER topchem 2006 comply with the FDA requirements) SUPERIOR EXCELLENT VERY GOOD GOOD MODERATE MECHANICAL THERMAL SEALABILITY Industries: INDUSTRY OIL & GAS ENERGY INFRASTRUCTURE PULP & PAPER TRANSPORT FOOD & BEVERAGES PHARMA
Typical technical data for thickness 2.0 mm: Compressibility ASTM F 36 M % 4 Recovery ASTM F 36 M % 40 Stress relaxation DIN 5293 30 MPa, 6 h/ C MPa 8 KLINGER cold/hot compression thickness decrease at 23 C % 2 MPa thickness decrease at 2 C % 40 Tightness DIN 28090-2 mg/s x m 0.0 Specific leakrate λ VDI 2440 mbar x l/s x m 3.60E-06 Thickness/weight increase H 2 SO 4, 00%: 8 h/23 C % HNO 3, 00%: 8 h/23 C % /2 NaOH, 33%: 72 h/0 C % / Density g/cm 3 3.0 Average surface resistance ρo Ω x0e3 Average specific volume resistance ρd Ω cm.2x0e3 Average dielectric strength E d kv/mm 6.7 Average power factor Hz tan δ 0.083 Average dielectric coefficient Hz εr 4.2 Thermal conductivity λ W/mK 0.40 ASME-Code sealing factors for gasket thickness.0 mm tightness class 0.mg/s x m MPa y 2 m 2.0 for gasket thickness 2.0 mm tightness class 0.mg/s x m MPa y 2 m 3. for gasket thickness 3.0 mm tightness class 0.mg/s x m MPa y 5 m 3.8 Dimensions of the standard sheets: Sizes: 0 x 0 mm Thicknesses:.0 mm,.5 mm, 2.0 mm, 3.0 mm Tolerances: Thickness acc. DIN 2809- Length mm, width mm Other thicknesses, sizes and tolerances on request. pt diagram for thickness 2.0 mm: 200 00 90 80 70 60 40 3 2 In area one, the gasket material is normally suitable subject to chemical compatibility. 2 3 In area two, the gasket material may be suitable but a technical evaluation is recommended. In area three, do not install the gasket without a technical evaluation. Always refer to the chemical resistance of the gasket to the media. 30 20 p i bar 200 00 0 C 00 200 2 Certified acc. to DIN EN ISO 900:2008 Subject to technical alterations. Status: March 206 Rich. Klinger Dichtungstechnik GmbH & Co KG» Am Kanal 8-0» A-2352 Gumpoldskirchen, Austria Tel +43 (0) 2252/62599-37» Fax +43 (0) 2252/62599-296» e-mail: marketing@klinger.co.at