ASSESSMENT OF THE USE OF METHYLAL AS HCFC REPLACEMENT IN PU FOAMS

Transcription

1 ASSESSMENT OF THE USE OF METHYLAL AS HCFC REPLACEMENT IN PU FOAMS PROPERTIES OF METHYLAL AND CURRENT USE Michel Beaujean Lambiotte & Cie, 18 Avenue des Aubépines, B-1180, Brussels, Belgium Tel : +32 (0) Fax : +32 (0) m.beaujean@lambiotte.com ABSTRACT Methylal is an economical physical blowing agent with good insulating properties and good toxicological, ecotoxicological and atmospheric behaviour. This paper describes its properties and its use as co-blowing agent. PROPERTIES OF METHYLAL IDENTIFICATION OF METHYLAL Methylal or dimethoxymethane (CH 3 -O-CH 2 -O-CH 3 ) is an acetal. It is sometimes described in the literature as an ether or a diether, but it is not. Methylal has different behaviours from ethers as detailed later. In Europe, Methylal has been REACH registered by Lambiotte & Cie (REACH reference number ) PRODUCTION OF METHYLAL BIO-SOURCING Raw materials used to produce Methylal are Methanol and Formaldehyde. Formaldehyde itself is produced from Methanol. Methanol finds its source in natural gas which is very abundant on the earth. Therefore, contrarily to other blowing agents like Pentanes, the production of Methylal doesn t consume non renewable oils. Moreover, Methylal is potentially bio-sourced if produced with bio-sourced Methanol. PHYSICAL-CHEMICAL PROPERTIES The boiling point of Methylal is 42 C which is ideal for a blowing agent. It s vapour pressure at 20 C is 44.0 kpa and kpa at 50 C. INSULATION PROPERTIES The thermal conductivity of Methylal in the gas phase at C is W/mK, which is lower than the thermal conductivity of Pentanes including Cyclopentane, as shown in Table 1. Product T T (10-2.W/m.K) ( C) (10-2.W/m.K) ( C) Methylal Pentane Isopentane Cyclopentane Table 1 : Thermal conductivities in gaseous phase FLAMMABILITY Methylal is flammable. In Europe, it belongs to the middle class of flammability. It is highly flammable. It is less flammable than n-pentane and Isopentane which are extremely flammable. Nevertheless, blends of polyols with useful amount of Methylal for polyurethane foams show high flash point. Moreover, blends of polyols with high amount of Methylal, above the quantity usually used for foam production, show a low combustion tendency.

2 TOXICOLOGY Methylal has a very well documented toxicological profile. Being REACH registered in Europe, all data required for a yearly production above 1000 tons are available. The results are very good. The TLV or MAK value in Germany of Methylal is 1000 ppm. This value has been reviewed by the German Authorities in , and has been confirmed at 1000 ppm. Methylal is not labelled for toxicological reasons. ECO-TOXICOLOGY Methylal has a good ecotoxicological profile. The WGK of Methylal (Wassergefährdungsklasse in Germany), which evaluates the toxicity of a chemical against water, is 1 on a scale from 0 to 3, 0 being non toxic. Methylal is also not labelled for eco-toxicological reasons. ATMOSPHERIC BEHAVIOUR The degradation of organic chemicals released in the atmosphere starts with their reaction with the hydroxyl radical. This reaction for Methylal is slow: 4.6 +/ cm³ molecule -1 s -1 (1). This rate is 14 times slower than expected by calculation if Methylal was considered as an ether. Methylal, if emitted in the atmosphere, will migrate to the upper layer before forming ozone and only make a moderate contribution to the formation of tropospheric ozone. Therefore Methylal has a low Photochemical Ozone Creation Potential (POCP). This is confirmed by its Californian Maximum Incremental Reactivity (MIR) of 0,89 (2). Its Global Warming Potential (GWP) is negligible. Nevertheless, its GWP is only 3/5 of the GWP of Pentanes because Methylal only contains 3 carbons and 2 oxygens. By definition, its Ozone Depletion Potential (ODP) is zero because Methylal doesn t contain any halogen atom. STABILITY Methylal is thermally stable for 7 days at 200 C. It is stable against peroxide formation. Without blanketing, there is no formation of peroxides after 1143 days. Methylal is also stable against hydrolysis. Acetals are stable in neutral and basic conditions, and may hydrolyse in aqueous acidic conditions. Nevertheless, Methylal shows a very slow rate of hydrolysis: there were no traces of hydrolysis after 1 year at ph level above 4. PROPERTIES OF POLYOLS-METHYLAL BLENDS MISCIBILITY Methylal is fully miscible with all polyols, including aromatic polyester polyols. VISCOSITY Methylal is a strong viscosity reducer. The reduction depends on the viscosity of the polyol itself: the higher the viscosity, the higher the reduction. Composition % w/w Viscosity (mpa.s) Polyol Methylal Tercarol 8092 (at 20 C) Polyol (visco at 22 C : 930 mpa.s) Table 2 : Viscosities of polyols-methylal blends

3 FLAMMABILITY Even if Methylal is flammable, once it is blended with polyols, the danger is strongly reduced. Blends of polyols with low percentage of methylal show high closed cup flash point as shown in Table 3. The flash point depends on the viscosity and/or the nature of the polyol: polyols of higher viscosities give higher flash points. Blend % (w/w) Polyol Methylal Polyol (visco at 22 C : 930 mpa.s) Tercarol 8092 (viscosity at 25 C: mpa.s) Flash point (closed cup) ( C) with Terate 2033 Terate 2541 Terate > > 70.0 > Table 3 : Closed cup flash point of polyol-methylal blends Blends with lower percentages of Methylal, which are very useful for the formulation, can avoid any flammability labelling. Blends of polyols with high percentage of Methylal show high open cup flash point as shown in Table 4. Blend polyol/methylal 92.5 / 7.5 w/w % Cleveland open cup flash point ( C) With a polyol for spray foam 64 With a polyol for panels 68 Table 4 : Open cup flash point of polyol-methylal blends COMBUSTIBILITY Blends of polyols with very high amount of Methylal, above the quantity usually used for foam production, show a low combustion tendency as shown in Table 5. In Europe, this point is very important for systems houses because European legislation (3) says that, if the flash point of a blend is between 21 C and 55 C but the blend doesn t contribute to the combustion, it doesn t need to be labelled as flammable. Blend % (w/w) Combustion description Polyol Methylal (in the presence of a flame) (visco 930 mpa.s) 98 2 No ignition 96 4 No ignition 94 6 No ignition 92 8 No ignition Single ignition of the vapours ; no further ignition in presence of a flame Ignition of the vapours ; can be repeated, but is self extinguishing Continuous burning Table 5 : Combustion of polyol-methlal blends

4 PROPERTIES OF ISOCYANATE-METHYLAL BLENDS Methylal is also miscible with isocyanates. Closed cup flash points of blends of isocyanate with a low percentage of methylal are high. Suprasec 5025 Methylal Closed cup flash point ( C) > METHYLAL FLAMMABILITY REDUCTION In systems, Methylal can be shared between the polyol and the isocyanate. Therefore, two blends of limited flammability are obtained instead of one blend with higher and one blend with lower flammability. METHYLAL IN COMBINATION WITH OTHER BLOWING AGENTS GENERAL ADVANTAGES TO USE METHYLAL In general, Methylal improves the miscibility, the foam uniformity and the flow. It reduces the size of the cells. It improves the adhesion and the insulation performance. It has also an influence on the pressure generated by the main blowing agent. Methylal is used with some blowing agents to reduce the cost. METHYLAL COMBINED WITH NORMAL PENTANE Methylal improves the miscibility of n-pentane in the polyol and in the mixture polyol isocyanate. This improvement is observed once Methylal is blended to the polyol or to the Pentane. Methylal makes the mixing of polyol, isocyanate and blowing agent easier at the mixing head. Due to the miscibility improvement, Methylal improves the foaming uniformity. The number of voids, pinholes, craters, lakes, etc. is reduced. Methylal reduces the size of the cells. Methylal improves the flow. It improves the adhesion on metallic surfaces. In blends with n-pentane, Methylal increases the pressure generated by n-pentane. The thermal conductivity of Methylal is lower than that of n-pentane, thus Methylal improves the insulation properties. METHYLAL COMBINED WITH CYCLOPENTANE Cyclopentane is generally used with a low boiling point hydrocarbon (e.g. Isopentane) to get more pressure in the blowing. Methylal also has a lower boiling point than Cyclopentane, and with its higher vapour pressure, also gives more pressure in replacement of Cyclopentane. Nevertheless, unlike Isopentane, the increase is not linear. At low percentage, Methylal gives as much pressure as Isopentane. Due to this pressure behaviour, Methylal in partial replacement of Cyclopentane increases the blowing rate and the compressive strength of the foam. Moreover, Methylal advantageously replaces Isopentane in these blends because additionally it brings the same advantages described above when combined with normal Pentane. Methylal in partial replacement of Cyclopentane improves the insulation properties of the foam. METHYLAL COMBINED WITH HFC-365mfc HFC-365mfc is promoted in combination with HFC-227ea as a non-flammable blend. HFC-227ea is used as a flame extinguisher for HFC-365mfc. Blends of polyol with or HFC-365mfc or Methylal have approximately the same open cup flash point. Blends polyol-hfc-365mfc (without HFC-227ea) Methylal can have high open cup flash point even with high amount of Methylal. Obviously, closed cup flash points are only high with low percentage of Methylal. A low percentage of Methylal in blends polyol + HFC-365mfc + HFC-227ea doesn t affect the flammability of the blend. In combination in low volumes with HFC-365mfc, Methylal decreases the condensation at low temperature in rigid foam cells, thus improving the thermal insulation. Fire performance is not affected by low percentage of Methylal. Methylal is used to decrease the formulation costs.

5 METHYLAL COMBINED WITH HFC-245fa HFC-245fa is used to avoid manipulation of flammable products and to provide non-flammability to the produced foam. Methylal, even being flammable, can partially substitute HFC-245fa keeping an acceptable flash point of the preblend with polyol, and not affecting the fire performance of the final foam. Blends polyol- Methylal-HFC-245fa show an optimum flash point, which is not at the lowest level of Methylal. Combined with HFC-245fa, the main function of Methylal is the reduction of cost. MARKET In Europe, Methylal is used in about twenty countries. It is used alone, or combined with water, HFC-365mfc, HFC-245fa, Cyclopentane or n-pentane. It is also used in combination with HCFC-141b, in countries where it is allowed to use it. Applications cover a wide range of products: blocks, panels, refrigeration, boilers, trucks, sprays, pipe insulation, flexible moulded foams, integral skin foams and one component foams. A significant part of the volume is used by system houses. CONCLUSION Methylal is an ecological and economical blowing agent with good technical performance. Blended with polyols, its flammability can be controlled. Methylal can be used as the only blowing agent in the formulation, but it also brings advantages in combination with all other blowing agents. BIBLIOGRAPHICAL NOTES 1 K.H Becker, I. Barnes, L. Thüner, Bergische Universität, Wuppertal, Germany. 2 California Air Resource Board (CARB) regulation for reducing the ozone formed from aerosol coating product emissions. 3 European Directive 2001/59/EC.